OB-OMEGABOND-AIR-SET

모델 보기

필터 또는 검색 기능을 사용하여 원하시는 모델을 찾으십시오.

총 5개의 상품

제품 번호 / 가격	Brand	Applications	Color	Dielectric Constant	Dielectric Strength Note	Features	Insulation Note	Material Construction Option	Mechanical Strength Properties	Mix Ratio By Weight	Operating Temperature, Max	Thermal Conductivity	Thermal Expansion Coefficient	Volume	Working Life	Modulus of Rupture	Kit Description	Density, Max	Modulus Of Elasticity
OB-500 POWDER105,320 원10 weeks리드타임은 상황에 따라 달라질 수 있습니다.	OMEGA Engineering	Casting, Coating, Dipping	Off white	-	Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil	Withstands short-tem immersion in molten metal; used as a coating on expendable thermocouple tubes	-	Coating Cement, Powder Part	Tensile Shear Strength: 1500 psi; Flexible Strength: 2000 psi; Compressive Strength: 1500 psi	2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight	1205 °C	-	10.93 x 10^-6 in/in/°F	8 oz	OMEGABOND 500® has a pot life of 1-hr after the powder and binder are mixed together; OB-500 reaches an initial air set after 4-hr at room temperature; a final set is only reached after oven baking at 55°C (130°F) for 4-hr; if the cement is to be used at temperatures above 100°C (212°F), OB-500 must under go an extended cure at 105°C (220°F) or above for 12 hours	-	-	Wet : 112 b/ft³ Dry : 82 b/ft³	3.6 x 10⁵ psi
OB-500 LIQUID가격 문의10 weeks리드타임은 상황에 따라 달라질 수 있습니다.	OMEGA Engineering	Casting, Coating, Dipping	Off white	-	Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil	Withstands short-tem immersion in molten metal; used as a coating on expendable thermocouple tubes	-	Coating Cement, Liquid part	Tensile Shear Strength: 1500 psi; Flexible Strength: 2000 psi; Compressive Strength: 1500 psi	2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight	1205 °C	-	10.93 x 10^-6 in/in/°F	8 oz	OMEGABOND 500® has a pot life of 1-hr after the powder and binder are mixed together; OB-500 reaches an initial air set after 4-hr at room temperature; a final set is only reached after oven baking at 55°C (130°F) for 4-hr; if the cement is to be used at temperatures above 100°C (212°F), OB-500 must under go an extended cure at 105°C (220°F) or above for 12 hours	-	-	Wet : 112 b/ft³ Dry : 82 b/ft³	3.6 x 10⁵ psi
OB-300105,320 원2 weeks리드타임은 상황에 따라 달라질 수 있습니다.	OMEGA Engineering	Bonding, Insulating, Sealing	Off white	3.5 to 6.0	Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil	Lower thermal conductivity and coefficient of thermal expansion	Volume Resistivity at 20°C: 10⁸-10⁹ ohm–cm;Volume Resistivity at 400°C: 10⁴-10⁵ ohm–cm;Volume Resistivity at 795°C: 10²-10³ ohm–cm	Low Expansion Cement	Tensile Shear Strength: 410 psi; Compressive Strength: 3900 psi; Shear Strength: 710 psi	1-part cement; just mix powder with water to a smooth, uniform consistency	980 °C	4 to 6 BTU-in/h-ft2-°F	6.2 x 10^-6 in/in/°F	8 oz	OMEGABOND 300® cures at room temperature by air drying in 18 to 24-hr, depending upon thickness and consistency; cure time can be accelerated by low temperature oven drying at 82°C (180°F); if the cement is to be exposed to elevated temperatures, cure for 18 to 24-hr at ambient temperature, then oven dry for 4-hr at 82°C (180°F) and for an additional 4-hr at 105°C (220°F), this helps to prevent spilling.	460 psi	-	-	-
OB-KIT-1167,150 원2 weeks리드타임은 상황에 따라 달라질 수 있습니다.	OMEGA Engineering	-	White	-	Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil	-	-	Air Set Cement Kit	-	2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight	0 °C	-	-	2 oz	-	-	Air set cement kit, ideal for research purposes; includes 2 fluid oz each of OB-300, OB-400, OB-500 powder and OB-500 liquid	-	-
OB-400105,320 원2 weeks리드타임은 상황에 따라 달라질 수 있습니다.	OMEGA Engineering	Coating, Embedding, Insulating	Tan to gray	3.4 to 4.5	Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil	Higher thermal conductivity and coefficient of thermal expansion; high maximum temperature rating	Volume Resistivity at 20°C: 10⁸-10⁹ ohm–cm;Volume Resistivity at 400°C: 10⁵-10⁶ ohm–cm;Volume Resistivity at 795°C: 10³-10⁴ ohm–cm	High Thermal Conductivity Cement	Tensile Shear Strength: 325 psi; Compressive Strength: 3300 psi; Shear Strength: 375 psi	1-part cement; just mix powder with water to a smooth, uniform consistency	1425 °C	11 BTU-in/h-ft2-°F	13.0 x 10^-6 in/in/°F	8 oz	OMEGABOND 400® cures at room temperature by air drying in 18 to 24-hr, depending upon thickness and consistency; cure time can be accelerated by low temperature oven drying at 82°C (180°F); if the cement is to be exposed to elevated temperatures, cure for 18 to 24-hr at ambient temperature, then oven dry for 4-hr at 82°C (180°F) and for an additional 4-hr at 105°C (220°F), this helps to prevent spilling.	-	-	-	-

스페이스를 누른 채 마우스 휠을 움직이면 표를 좌우로 스크롤할 수 있습니다.

제품 번호 / 가격

Brand

Applications

Color

Dielectric Constant

Dielectric Strength Note

Features

Insulation Note

Material Construction Option

Mechanical Strength Properties

Mix Ratio By Weight

Operating Temperature, Max

Thermal Conductivity

Thermal Expansion Coefficient

Volume

Working Life

Modulus of Rupture

Kit Description

Density, Max

Modulus Of Elasticity

수량 / 장바구니

OB-500 POWDER105,320 원10 weeks리드타임은 상황에 따라 달라질 수 있습니다.

OMEGA Engineering

Casting, Coating, Dipping

Off white

Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil

Withstands short-tem immersion in molten metal; used as a coating on expendable thermocouple tubes

Coating Cement, Powder Part

Tensile Shear Strength: 1500 psi; Flexible Strength: 2000 psi; Compressive Strength: 1500 psi

2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight

1205 °C

10.93 x 10^-6 in/in/°F

8 oz

OMEGABOND 500® has a pot life of 1-hr after the powder and binder are mixed together; OB-500 reaches an initial air set after 4-hr at room temperature; a final set is only reached after oven baking at 55°C (130°F) for 4-hr; if the cement is to be used at temperatures above 100°C (212°F), OB-500 must under go an extended cure at 105°C (220°F) or above for 12 hours

Wet : 112 b/ft³ Dry : 82 b/ft³

3.6 x 10⁵ psi

OB-500 LIQUID가격 문의10 weeks리드타임은 상황에 따라 달라질 수 있습니다.

OMEGA Engineering

Casting, Coating, Dipping

Off white

Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil

Withstands short-tem immersion in molten metal; used as a coating on expendable thermocouple tubes

Coating Cement, Liquid part

Tensile Shear Strength: 1500 psi; Flexible Strength: 2000 psi; Compressive Strength: 1500 psi

2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight

1205 °C

10.93 x 10^-6 in/in/°F

8 oz

Wet : 112 b/ft³ Dry : 82 b/ft³

3.6 x 10⁵ psi

OB-300105,320 원2 weeks리드타임은 상황에 따라 달라질 수 있습니다.

OMEGA Engineering

Bonding, Insulating, Sealing

Off white

3.5 to 6.0

Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil

Lower thermal conductivity and coefficient of thermal expansion

Volume Resistivity at 20°C: 10⁸-10⁹ ohm–cm;Volume Resistivity at 400°C: 10⁴-10⁵ ohm–cm;Volume Resistivity at 795°C: 10²-10³ ohm–cm

Low Expansion Cement

Tensile Shear Strength: 410 psi; Compressive Strength: 3900 psi; Shear Strength: 710 psi

1-part cement; just mix powder with water to a smooth, uniform consistency

980 °C

4 to 6 BTU-in/h-ft2-°F

6.2 x 10^-6 in/in/°F

8 oz

OMEGABOND 300® cures at room temperature by air drying in 18 to 24-hr, depending upon thickness and consistency; cure time can be accelerated by low temperature oven drying at 82°C (180°F); if the cement is to be exposed to elevated temperatures, cure for 18 to 24-hr at ambient temperature, then oven dry for 4-hr at 82°C (180°F) and for an additional 4-hr at 105°C (220°F), this helps to prevent spilling.

460 psi

OB-KIT-1167,150 원2 weeks리드타임은 상황에 따라 달라질 수 있습니다.

OMEGA Engineering

White

Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil

Air Set Cement Kit

2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight

0 °C

2 oz

Air set cement kit, ideal for research purposes; includes 2 fluid oz each of OB-300, OB-400, OB-500 powder and OB-500 liquid

OB-400105,320 원2 weeks리드타임은 상황에 따라 달라질 수 있습니다.

OMEGA Engineering

Coating, Embedding, Insulating

Tan to gray

3.4 to 4.5

Dielectric Strength at 20°C:12.5 to 51.0 V/mil;Dielectric Strength at 400°C: ≤15 V/mil;Dielectric Strength at 795°C: ≤1.3 V/mil

Higher thermal conductivity and coefficient of thermal expansion; high maximum temperature rating

Volume Resistivity at 20°C: 10⁸-10⁹ ohm–cm;Volume Resistivity at 400°C: 10⁵-10⁶ ohm–cm;Volume Resistivity at 795°C: 10³-10⁴ ohm–cm

High Thermal Conductivity Cement

Tensile Shear Strength: 325 psi; Compressive Strength: 3300 psi; Shear Strength: 375 psi

1-part cement; just mix powder with water to a smooth, uniform consistency

1425 °C

11 BTU-in/h-ft2-°F

13.0 x 10^-6 in/in/°F

8 oz

OMEGABOND 400® cures at room temperature by air drying in 18 to 24-hr, depending upon thickness and consistency; cure time can be accelerated by low temperature oven drying at 82°C (180°F); if the cement is to be exposed to elevated temperatures, cure for 18 to 24-hr at ambient temperature, then oven dry for 4-hr at 82°C (180°F) and for an additional 4-hr at 105°C (220°F), this helps to prevent spilling.